To prepare miscible polyethylene glycol diacrylate/polyvinylidene fluoride ~PEGDA/PVdF! blend gel polymer electrolytes, low molecular weight (M 5 742) liquid PEGDA oligomer was mixed with PVdF-HFP dissolved in ethylene carbonate/dimethyl carbonate/LiPF6 liquid electrolytes, and then cured under ultraviolet irradiation. Room temperature conductivity of PEGDA/PVdF blend films was found to be comparable to that of PVdF-HFP gel polymer electrolytes, and they were electrochemically stable up to 4.6 V vs. Li/Li1. Scanning electron micrographs revealed that PEGDA/PVdF blend electrolytes have pore size intermediate between dense PEGDA and highly porous PVdF-HFP. It was confirmed by weight change measurement that liquid electrolyte was likely to evaporate through large pores in PVdF-HFP at 80째C, while PEGDA/PVdF blend showed better liquid electrolyte retention ability. This result was in good agreement with more stable interfacial properties of PEGDA/PVdF blend at 80째C in ac impedance analysis. Consequently, both PVdF-HFP and PEGDA/PVdF gel polymer electrolytes delivered similar discharge capacity at room temperature, but PEGDA/PVdF blend gel polymer electrolyte showed much better cycle performance than pure PVdF-HFP at 80째C.....